| Notices |
Welcome to the new PGCA Forum! As well, since it
is new - please read the following:
This is a new forum - so you must REGISTER to this Forum before posting;
If you are not a PGCA Member, we do not allow posts selling, offering or brokering firearms and/or parts; and
You MUST REGISTER your REAL FIRST and LAST NAME as your login name.
To register:
Click here..................
If you are registered to the forum and keep getting logged
out: Please
Click Here...
Welcome & enjoy!
To read the Posts, Messages & Threads in the PGCA Forum, you must be REGISTERED and LOGGED INTO your account!
To Register, as a New User please see the Registration Link Above. If you are registered, but not Logged In, please Log in with your account Username and Password found on this page to the top right.
|
06-27-2011, 08:40 PM
|
#3
|
Member
|
|
|
|
Member Info
|
Join Date: Nov 2008
Posts: 2,387
Thanks: 1,287
Thanked 3,929 Times in 1,067 Posts
|
|
Quote:
Originally Posted by william faulk
Note that the hammer faces on my 1892 top lever are showing ever deepening indentions where the hammers strike the pins.Is the metal getting soft with age ?
Do you find some one that caps the hammer faces of rehardens the hammers ?
I have noticed indentions are becoming wider and more pronounced each year..any advice ?  |
I had a similar problem with the hammmer faces of a Wm. Powell & Sons .410 back-action hammergun that Turnbull Restorations hardened with satisfactory results.
__________________
Wild Skies
Since 1951
|
|
|
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -4. The time now is 07:32 AM.
Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2025, Jelsoft Enterprises Ltd.
Copyright © 1998 - 2025, Parkerguns.org Copyright © 2004 Design par Megatekno - 2008 style update 3.7 avec l'autorisation de son auteur par Stradfred.
|
Threaded Mode