| Notices |
Welcome to the new PGCA Forum! As well, since it
is new - please read the following:
This is a new forum - so you must REGISTER to this Forum before posting;
If you are not a PGCA Member, we do not allow posts selling, offering or brokering firearms and/or parts; and
You MUST REGISTER your REAL FIRST and LAST NAME as your login name.
To register:
Click here..................
If you are registered to the forum and keep getting logged
out: Please
Click Here...
Welcome & enjoy!
To read the Posts, Messages & Threads in the PGCA Forum, you must be REGISTERED and LOGGED INTO your account!
To Register, as a New User please see the Registration Link Above. If you are registered, but not Logged In, please Log in with your account Username and Password found on this page to the top right.
|
03-28-2021, 11:08 PM
|
#7
|
Member
|
|
|
|
Member Info
|
Join Date: Nov 2008
Posts: 4,995
Thanks: 554
Thanked 15,704 Times in 2,676 Posts
|
|
The results of tests on the various Parker barrel steels demonstrated that there were slight differences within the broader range of barrel steels. Those results were published in the Parker Pages and discussed here numerous times . I think this was about ten years ago that the old inaccurate suggestion that the barrel steels were the same was put to rest. I am surprised to see it surface again. There is always somebody who does not get the word.
The barrels were sourced from various manufacturers .
|
|
|
|
The Following 2 Users Say Thank You to Bruce Day For Your Post:
|
|
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -4. The time now is 09:50 PM.
Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2025, Jelsoft Enterprises Ltd.
Copyright © 1998 - 2025, Parkerguns.org Copyright © 2004 Design par Megatekno - 2008 style update 3.7 avec l'autorisation de son auteur par Stradfred.
|
Threaded Mode