Default

In my opinion, it would be foolish to spend another dime on this gun. Any annealing will soften it, but it will erase any 'memory'. Annealing it would only soften it so that it could be mechanically manipulated, and that's a total black hole. I say this because I spent over 30 years making steel, then heat treating it. If a casting warped in heat treat, it was always possible to anneal, straighten, and re-heat treat. All luxuries I may have had are lost once a part is finish machined.
edgarspencer is offline  
The Following 10 Users Say Thank You to edgarspencer For Your Post:
 


Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -4. The time now is 12:08 PM.

Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2025, Jelsoft Enterprises Ltd.
Copyright © 1998 - 2025, Parkerguns.org
Copyright © 2004 Design par Megatekno
- 2008 style update 3.7 avec l'autorisation de son auteur par Stradfred.