Quote:
Originally Posted by Virginia Hessler View Post
I would rather see a little blue instead of jet black.

Can anyone suggest a different solution to try ?

Thank you, Tom
Tom, it's your gun so if you don't want it to look as it did when it originally left the factory that's your choice - make it blue... but its value will be somewhat negatively affected by refinishing the barrels incorrectly.
Dean Romig is online now   Reply With Quote
The Following 2 Users Say Thank You to Dean Romig For Your Post:
Old 08-30-2014, 08:49 PM   #2
Member
Autumn Daze
PGCA Lifetime
Member
 
Dave Suponski's Avatar

Member Info
 
Join Date: Nov 2008
Posts: 5,915
Thanks: 4,389
Thanked 4,112 Times in 1,744 Posts

Default

Also one thing to remember about reblueing barrels is that the lower grade guns such as a Vulcan grade should not have the barrels polished to a high sheen before bluing.So that as much of the original striking marks as possible remain.
__________________
"Much care is bestowed to make it what the Sportsman needs-a good gun"-Charles Parker
Dave Suponski is offline   Reply With Quote
The Following 4 Users Say Thank You to Dave Suponski For Your Post:
Reply


Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -4. The time now is 01:10 PM.

Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2025, Jelsoft Enterprises Ltd.
Copyright © 1998 - 2025, Parkerguns.org
Copyright © 2004 Design par Megatekno
- 2008 style update 3.7 avec l'autorisation de son auteur par Stradfred.