| Notices |
Welcome to the new PGCA Forum! As well, since it
is new - please read the following:
This is a new forum - so you must REGISTER to this Forum before posting;
If you are not a PGCA Member, we do not allow posts selling, offering or brokering firearms and/or parts; and
You MUST REGISTER your REAL FIRST and LAST NAME as your login name.
To register:
Click here..................
If you are registered to the forum and keep getting logged
out: Please
Click Here...
Welcome & enjoy!
To read the Posts, Messages & Threads in the PGCA Forum, you must be REGISTERED and LOGGED INTO your account!
To Register, as a New User please see the Registration Link Above. If you are registered, but not Logged In, please Log in with your account Username and Password found on this page to the top right.
|
05-23-2014, 02:41 PM
|
#7
|
Member
|
|
|
|
Member Info
|
Join Date: Nov 2008
Posts: 4,995
Thanks: 554
Thanked 15,701 Times in 2,676 Posts
|
|
Yes that can be done. I saw a set at Dales where the owner had done just that.
But there had been a slight error. The steel was etched down below the level of the iron and the resultant surface was highly uneven. The barrels would have had to be draw filed again and carded again to get smooth. I guess the owner had tried his hand at it and sent them to Dale. Too bad at one time they had been nice barrels.
|
|
|
|
The Following 2 Users Say Thank You to Bruce Day For Your Post:
|
|
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -4. The time now is 10:21 AM.
Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2025, Jelsoft Enterprises Ltd.
Copyright © 1998 - 2025, Parkerguns.org Copyright © 2004 Design par Megatekno - 2008 style update 3.7 avec l'autorisation de son auteur par Stradfred.
|
Threaded Mode