| Notices |
Welcome to the new PGCA Forum! As well, since it
is new - please read the following:
This is a new forum - so you must REGISTER to this Forum before posting;
If you are not a PGCA Member, we do not allow posts selling, offering or brokering firearms and/or parts; and
You MUST REGISTER your REAL FIRST and LAST NAME as your login name.
To register:
Click here..................
If you are registered to the forum and keep getting logged
out: Please
Click Here...
Welcome & enjoy!
To read the Posts, Messages & Threads in the PGCA Forum, you must be REGISTERED and LOGGED INTO your account!
To Register, as a New User please see the Registration Link Above. If you are registered, but not Logged In, please Log in with your account Username and Password found on this page to the top right.
|
12-17-2024, 07:34 PM
|
#11
|
Member
|
|
|
|
Member Info
|
Join Date: Sep 2011
Posts: 6,922
Thanks: 3,578
Thanked 14,358 Times in 3,742 Posts
|
|
The shell rim ring etched into the breech face is quite severe, and puzzling.
Obviously, it was caused by a shell, but how? Was a shell left in the right barrel for a long time? Was there some interaction of the corrosive primer material and the brass head of the shell. This is a reach, but was the gun left leaning against any electrical component? I say this because it appears as though there was some galvanic action taking place. Can you see why old engineers are so anal?
|
|
|
|
The Following 6 Users Say Thank You to edgarspencer For Your Post:
|
|
|
|
Posting Rules
|
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts
HTML code is Off
|
|
|
All times are GMT -4. The time now is 10:22 AM.
Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2026, Jelsoft Enterprises Ltd.
Copyright © 1998 - 2026, Parkerguns.org Copyright © 2004 Design par Megatekno - 2008 style update 3.7 avec l'autorisation de son auteur par Stradfred.
|
Threaded Mode