Brian, Hi-temp Hi-force 44 melts at 650f. Two different solders.
|
||||||
|
|
||||||
 |
 |
 |
|
|
|
10-02-2015, 11:19 AM
|
#14 | ||||||
|
Is my math right? Is that a round every 3.5 seconds for 2.5 hours? That's incredible!
|
||||||
|
|
|
||||||
|
|
|
|
|
|
10-02-2015, 11:19 AM
|
#15 | ||||||
|
Gotcha. Missed the high temp part. Thanks for clarifying.
__________________
B. Dudley |
||||||
|
|
|
||||||
|
|
|
|
|
|
10-16-2015, 04:59 PM
|
#16 | ||||||
|
Your forend wood will burst into flames (or the multi-trap will seize) before you ever remotely approach the temps required to melt the solder used to hold your barrels together.
|
||||||
|
|
|
||||||
|
|
|
| The Following User Says Thank You to Kevin McCormack For Your Post: |
|
|
|
10-17-2015, 04:10 PM
|
#17 | ||||||
|
Standard 60/40 tin-lead solder melts at 360f.
|
||||||
|
|
|
||||||
|
|
|
|
|
|
10-17-2015, 07:36 PM
|
#18 | ||||||
|
. . . and wood will burst into flames at 572 degrees fahrenheit.
__________________
Wild Skies Since 1951 |
||||||
|
|
|
||||||
|
|
|
| The Following User Says Thank You to Greg Baehman For Your Post: |
|
solder | |
|
10-28-2015, 06:09 PM
|
#19 | ||||||
|
solder
Anyone where to get 60/40 or 50/50 lead solder, all I can find is lead free, it does not flow or hold as well as lead tin.
Ron Moore |
||||||
|
|
|
||||||
|
|
|
|
|
|
10-28-2015, 07:40 PM
|
#20 | ||||||
|
eBay does pretty well with it. Search for solder and stained glass. The suppliers for stained glass cameing have some great choices for a few great ratios. You will just need your own flux. The solder is not cored. I have had good luck with Avril 63/37. Avril has 50/50 and 60/40 too.
|
||||||
|
|
|
||||||
|
|
|
 |
|
|