Eric, I've made springs for muzzleloading locks, and sometimes for my SxS's. The draw temps would be below the CCHing temps [ IMO ] so I believe all parts are removed before CChing. The hammers and sears are also hardend and I think the temp from CCHing would ruin them. Maybe Brad will reply. Paul