Wrought iron is softer than steel but due to its inclusions it doesnt machine as well. It can very quickly dull cutting tools and perhaps this is why someone would avoid damascus. I would agree that liability is a more likely concern and certainly so for dent raising, but the cost of the tooling isnt a small matter especially when the operator is doing high quality work at bottom line prices.