Pitting always looks worse than it is, generally speaking. You are looking across it, not down onto it. I have been amazed what can be completely removed by honing with proper equipment with only a few thousandths of material being removed.

I can certainly saw that any usual amount of pitting near the breech will not cause any safety concerns. Out in the thinner areas of the barrels is where it can be a concern. Careful measuring with a good wall thickness gauge is the only way of knowing, and even then it only gives you an idea of what is going on.
__________________
B. Dudley
Brian Dudley is offline   Reply With Quote
The Following 6 Users Say Thank You to Brian Dudley For Your Post:
Visit Brian Dudley's homepage!
 

Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -4. The time now is 04:41 PM.

Powered by vBulletin® Version 3.8.4
Copyright ©2000 - 2025, Jelsoft Enterprises Ltd.
Copyright © 1998 - 2025, Parkerguns.org
Copyright © 2004 Design par Megatekno
- 2008 style update 3.7 avec l'autorisation de son auteur par Stradfred.