Bill and Chuck, remember the Parker letter that John Davis published on this website that essentially stated that in order of barrel wear resistance, from most easily worn to most wear resistant, it was
damascus
Bernard
Acme
Acme was the only fluid steel grade considered. Likely wear resistance equates to hardness and dent resistance as well.