Dean, I would agree that the heat didn't play a part in this from a metallurgical point, as it would need to get above about 900 degrees F, the lower critical temperature for alloy steel, but I think if the case can be made that the cleaning agent played a part, the heating of that agent would most likely intensify the etching effect.