Welcome to the new PGCA Forum! As well, since it
is new - please read the following:
This is a new forum - so you must REGISTER to this Forum before posting;
If you are not a PGCA Member, we do not allow posts selling, offering or brokering firearms and/or parts; and You MUST REGISTER your REAL FIRST and LAST NAME as your login name.
To register: Click here..................
If you are registered to the forum and keep getting logged
out: Please
Click Here...
Welcome & enjoy!
To read the Posts, Messages & Threads in the PGCA Forum, you must be REGISTERED and LOGGED INTO your account! To Register, as a New User please see the Registration Link Above. If you are registered, but not Logged In, please Log in with your account Username and Password found on this page to the top right.
It looks like they got the joint too hot & burnt the flux causing a weak joint. More that likely the repoductions were all soft soldered. And the reason we haven't seen more failures is most are shot very little, if at all. I've had 9 repo's over the years & most only had a few boxes shot through them, & then into the safe they go & a few were never shot at all. Most that come up for sale look like they have never been shot. So, this is probably why we haven't seen many failures.