Welcome to the new PGCA Forum! As well, since it
is new - please read the following:
This is a new forum - so you must REGISTER to this Forum before posting;
If you are not a PGCA Member, we do not allow posts selling, offering or brokering firearms and/or parts; and You MUST REGISTER your REAL FIRST and LAST NAME as your login name.
To register: Click here..................
If you are registered to the forum and keep getting logged
out: Please
Click Here...
Welcome & enjoy!
To read the Posts, Messages & Threads in the PGCA Forum, you must be REGISTERED and LOGGED INTO your account! To Register, as a New User please see the Registration Link Above. If you are registered, but not Logged In, please Log in with your account Username and Password found on this page to the top right.
I measure lots of (softer than AISI 1010 and up) pattern welded barrels and my 'tip' is brass. I can point it up as needed with use.
I agree with Garhart that it is very difficult to a. get into pits and b. know if you are at the bottom of the pit.
Which is also why a full evaluation should include bore visualization with a rigid or fiberoptic bore scope.