How NOT to case harden a Parker
Unread 07-27-2020, 08:18 PM   #1
Member
Andy Clark
PGCA Lifetime
Member
 
Andrew Clark's Avatar

Member Info
 
Join Date: Mar 2017
Posts: 90
Thanks: 357
Thanked 275 Times in 53 Posts

Default How NOT to case harden a Parker

This forend iron belongs to a Parker that was restored and color case hardened by a well know company here in the Northeast that will remain unnamed. I purchased the gun a couple years ago. 2 weeks ago I decided to take it out and shoot a couple boxes through it. Upon taking the gun apart to clean and put away I noticed these cracks in the forend iron. My first course of action was to completely disassemble the gun to examine it for other fractures or cracks. I could not see any other visible damage but was highly concerned. I called a metallurgist friend who owns a machine shop in my town. He agreed to examine the frame and forend iron. Not only did he find the forend iron was through hard, he also found the frame to be equally as hard and the roll joint was fractured as well. I then brought the parts to a local gunsmith to have the parts annealed so Fred could magnaflux the parts. Fortunately all the parts are fine except the forend iron and joint roll. The forend iron has already been mapped on the optical comparator and is going in the gas box tomorrow to be micro tog welded. I intentionally am posting pictures of the annealed parts so as not to give away the obvious. I guess the moral is be very careful when it comes to re-case hardening parts!
Attached Images
File Type: jpg 20200726_070733.jpg (490.9 KB, 9 views)
File Type: jpg 20200726_070754.jpg (351.2 KB, 7 views)
File Type: jpg 20200726_070830.jpg (383.3 KB, 8 views)
Andrew Clark is offline   Reply With Quote
The Following 7 Users Say Thank You to Andrew Clark For Your Post:
Unread 07-28-2020, 07:23 AM   #2
Member
Mills
PGCA Lifetime Member
Since 3rd Grade
 
Mills Morrison's Avatar

Member Info
 
Join Date: Nov 2011
Posts: 10,302
Thanks: 14,183
Thanked 12,306 Times in 4,411 Posts

Default

Yikes
Mills Morrison is offline   Reply With Quote
Unread 07-28-2020, 08:14 AM   #3
Member
chris dawe
PGCA Member
 
chris dawe's Avatar

Member Info
 
Join Date: Aug 2010
Posts: 1,171
Thanks: 2,576
Thanked 2,783 Times in 601 Posts

Default

For what its worth ,I've seen more than one forend irons cracked in that exact spot that had not been in an oven since they left Parker ...the roll joint I have not seen cracked
chris dawe is offline   Reply With Quote
The Following 4 Users Say Thank You to chris dawe For Your Post:
Unread 07-28-2020, 09:17 AM   #4
Member
Louis Rotelli
Forum Associate

Member Info
 
Join Date: Jan 2017
Posts: 48
Thanks: 0
Thanked 94 Times in 37 Posts

Default

I have come across a few other forend iron which cracked after Color casing. The issue is they were probably either not annealed prior to re case hardening or they were brought up to too high a temperature. I also had a forend latch break in half when I was making a new forend and carefully tapped the latch in to the wood with a rawhide mallet.
Louis Rotelli is offline   Reply With Quote
The Following 2 Users Say Thank You to Louis Rotelli For Your Post:
Unread 07-29-2020, 12:05 AM   #5
Member
Jim DiSpagno
Forum Associate

Member Info
 
Join Date: Jul 2009
Posts: 1,840
Thanks: 5
Thanked 2,559 Times in 773 Posts

Default

Metal fatigue
Jim DiSpagno is offline   Reply With Quote
Unread 07-29-2020, 09:11 PM   #6
Member
Allen Gill
Forum Associate

Member Info
 
Join Date: May 2018
Posts: 29
Thanks: 71
Thanked 75 Times in 17 Posts

Default

Appears to be quench cracks. I've seen a few. They like to begin at stress risers like holes and radii.
Allen Gill is offline   Reply With Quote
The Following User Says Thank You to Allen Gill For Your Post:
Unread 07-31-2020, 11:38 AM   #7
Member
GH-16
PGCA Member

Member Info
 
Join Date: Nov 2009
Posts: 1,002
Thanks: 5,111
Thanked 1,304 Times in 445 Posts

Default

I've seen two forearm irons crack in the same area that hadn't been re-case hardened. One was on a GHE-20ga that I was purchasing from a well known dealer in Parkers that had done some work to the gun himself.

When I was buying that gun & it was in the inspection period. I found a crack in the forearm iron at the exact spot this iron is cracked. I liked the gun and decided to call Brad Bachelder to get his advice on if the crack was repairable. Brad explained that it's fairly common to see cracks at that thin spot, his opinion based on some of his experiences was that a good portion of the irons cracking in that location was due to over tightening the iron mounting screws and poor wood to metal fit where the iron is bedded in the wood. These are old guns, wood can shrink, change shape, get oil soaked & people work on the guns which can change fit as time goes on. Brad told me that even he had cracked a couple of irons in that location until he figured out what to watch out for when assembling a Parker forearm.

I'm not saying the OP's take about his forearm being over hardened isn't correct, I'm just giving a different perspective based on my experiences and Brad's knowledge he shared with me.

Brad repaired that GHE forearm with laser welding and you couldn't tell where it was repaired.
Paul Ehlers is offline   Reply With Quote
The Following 2 Users Say Thank You to Paul Ehlers For Your Post:
Unread 10-04-2020, 09:29 AM   #8
Member
BRDHNTR
PGCA Lifetime
Member

Member Info
 
Join Date: Nov 2012
Posts: 3,745
Thanks: 7,176
Thanked 2,695 Times in 1,233 Posts

Default

Brad was an absolute gentleman, highly skilled at his craft and great to work with.
allen newell is offline   Reply With Quote
The Following 2 Users Say Thank You to allen newell For Your Post:
Unread 10-04-2020, 05:50 PM   #9
Member
Kevin McCormack
PGCA Lifetime
Member

Member Info
 
Join Date: Jun 2009
Posts: 2,006
Thanks: 1,218
Thanked 3,599 Times in 1,016 Posts

Default

I would fire up the WayBack machine and journey to c. 1919 Meriden for a sit-down with the Storm brothers, originators and perfectors of the mesmerizing "oil on water" sheen achieved on the old jewels.
Kevin McCormack is offline   Reply With Quote
The Following User Says Thank You to Kevin McCormack For Your Post:
Unread 10-05-2020, 04:37 PM   #10
Member
Craig Budgeon
PGCA Member

Member Info
 
Join Date: Jan 2016
Posts: 479
Thanks: 123
Thanked 341 Times in 207 Posts

Default

I suspect the forend iron cracked for the same reason that Parker added a radius to there early hammer gun receivers. I believe it could be avoided by design, depth of carbon (case), and by quenching temperature. Annealing doesn't reduce the depth of carbon, but will reduce the hardeness.
Craig Budgeon is offline   Reply With Quote
Reply

Thread Tools
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -4. The time now is 12:12 PM.

Powered by vBulletin® Version 3.8.4