#3 | ||||||
|
![]()
SxS:
Much depends on the type and age of the gun in question. But, in general, yes. Both tubes should be within a couple of thousandths of the same spec. But remember... you a talking about a shotgun. It is intended to throw a cloud of pellets. and the charge expands to fill the bore on its way out - which is the principle of back boring. A little "tolerance" is not going to matter. In the final analysis, the more metal you have in a SxS shotgun tube, the better. General rule. So... if one tube is thicker than the other, be grateful. And yes, it could well be the result of responsible honing that took out only as much metal as needed. Bottom line: Don't let any of this worry you. |
||||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
#4 | ||||||
|
![]()
But always be certain of the barrel wall thickness before you buy a gun with questionable bore diameters.
|
||||||
![]() |
![]() |
![]() |
![]() |
![]() |
The Following 4 Users Say Thank You to Dean Romig For Your Post: |
![]() |
![]() |
![]() |
#5 | ||||||
|
![]()
I agree that generally each bore should be within say .003" diameter of the other. But keep in mind that most shotgun makers bought rough tubes to their individual specs from suppliers, and an overrun for one maker could be a bargain buy for another maker. And thus, tubes with different bore diameters could find their way to the storage racks of some of the makers. Generally the barrel assembler would choose two tubes of like bore diameter for a barrel set but that may not have happened all the time. For example: an Ithaca 16 gauge on my bench now that has right tube at .685" bore diameter and choke .671 = .014" constriction. Left tube .674 bore diameter and choke .646 = .028" constriction. Gun is stamped 2 & 4 indicating Mod & Full and the choke diameters are spot on. This gun is absolutely "factory".
For those not familiar with barrel honing (not backboring) it can only be done UNIFORMLY using a Sunnen barrel hone or equivalent machine tool, and they are very expensive and not usually found in the shops of gunsmiths. Most gunsmiths used/use simplistic tools to "hone barrels" - such as emery cloth on the end of a mandrel spun by a drill motor or maybe a lathe. This does not produce UNIFORM bores. Therefore if you're reading larger-smaller-larger (variable bore) with your barrel mike, it's probably been "honed" by some gunsmith using emery cloth or similar. But if your mike is showing one bore is larger than the other, but it's UNIFORM to within .001" diameter along its entire run, that barrel is likely factory. The other possibility is it's been backbored using a lathe and reamer(s) but in that case a close visual inspection will show a difference in surface finish/appearance from one bore to the other. Just my take on it fwiw. |
||||||
![]() |
![]() |
![]() |
![]() |
![]() |
The Following 4 Users Say Thank You to Frank Srebro For Your Post: |
![]() |
![]() |
![]() |
#6 | ||||||
|
![]()
I have always believed that Parker Bros. would rebore a barrel to achieve the desired choke/pattern/pellet count. And that would account at least partially for the varience we often see in Parker bore diameters.
__________________
"Much care is bestowed to make it what the Sportsman needs-a good gun"-Charles Parker |
||||||
![]() |
![]() |
![]() |
![]() |
![]() |
The Following 4 Users Say Thank You to Dave Suponski For Your Post: |
![]() |
![]() |
![]() |
#7 | ||||||
|
![]()
I wonder if bore variation on a SXS is normal and we don't see it because we don't look or is it something that we should be concerned about?
When does a variation get "out of limits"....001, 002, 003" in or whatever? Thanks for your consideration Linn |
||||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
#8 | ||||||
|
![]()
I'm not sure of what you mean by " out of limits ". As stated previously, there are reasons for a difference and as long as the barrels are thick enough there's really not a reason to worry about it.
__________________
Paul Harm |
||||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
#9 | ||||||
|
![]()
What I meant by "out of limits" comes from my belief that when newly made a shotgun barrel has specifications--- like .650 plus or minus .002. This means it could be .648 to .650 and still could be within specification. This is not so??
|
||||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
#10 | ||||||
|
![]()
Parker bores from side to side, in my experience, vary little, a thousandth or two at the most. If I see a .003 variance, I suspect that the bores have been cleaned up.
|
||||||
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|